Mg‐Zr合金の結晶粒微細化機構と鋳造組織
スポンサーリンク
概要
- 論文の詳細を見る
The investigation was performed to examine the influence of undissolved Zr particles in molten magnesium on the grain refinement of Mg–Zr alloy. A Mg–30%Zr master alloy was added to the molten pure magnesium at 993 K. All samples revealed that 0.4%Zr was dissolved in the pure magnesium. Sedimentation of Zr particles occured for holding the molten magnesium up to 7.2 ks at the temperature of 993 K and the grain size of the solidified structure became larger with prolonging holding time. However, when the molten metal was agitated just before pouring, grain refinement always occured. It is suggested that the undissolved Zr particles in the melt are nucleation sites of the solidifying magnesium or primary zirconium crystals. Zr content was the lowest around the undissolved Zr particles observed in Zr–enriched cored structure, because the undercooling occured for growth of the predendritic region.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.