6063アルミニウム合金鋳塊におけるAl‐Fe‐Si系晶出相の種類に及ぼす均質化処理の影響
スポンサーリンク
概要
- 論文の詳細を見る
The effect of homogenizing treatment on the type of Al–Fe–Si intermetallic compound phases in 6063 aluminum alloys was investigated using X-ray diffraction and transmission electron microscopy (TEM). The four kinds of alloys containing 0.1 to 0.5 mass%Fe were melted and then cooled at three cooling rates ranging from 0.06 to 50 K/s, followed by the homogenization at 858 K for 54 ks and 2.4 Ms. The Al–Fe–Si compound particles were extracted from the alloy ingots using the thermal phenol method. A large amount of the β phases (monoclinic: a=b=0.612 nm, c=4.15 nm, β=91°) were found in the ingot containing 0.1 mass%Fe obtained by casting cooling rate of 0.06 K/s. When that ingot was homogenized at 858 K for 54 ks and 2.4 Ms, the amount of the β phases had a tendency to decrease, and that of the α' phases (hexagonal: a=1.23 nm, c=2.62 nm) had a tendency to increase. Moreover, a large amount of the α phases (cubic: a= 1.252 nm or 1.256 nm) were found in the ingot containing 0.5 mass%Fe obtained by casting cooling rate of 50 K/s. When that ingot was homogenized at 858 K for 54 ks, a large amount of the α phases remained like the as-cast ingot. However, in that ingot homogenized at 858 K for 2.4 Ms, the main Al–Fe–Si compound particles changed from the α phase to the α' phase. In the 0.2 mass%Fe ingot at the casting cooling rate of 5 K/s, as solidified condition of commercial alloys, the β phase gradually decreased and the relative frequency of the α phase increased from 10% to 40% in homogenizing at 858 K for 54 ks. However, that of the α' phase also increased to 50% in homogenized ingot. Furthermore, in that ingot homogenized at 858 K for 2.4 Ms, almost all the Al–Fe–Si compound particles were the α' phase.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.