6061アルミニウム合金とSUS304ステンレス鋼の摩擦圧接部組織
スポンサーリンク
概要
- 論文の詳細を見る
A 6061 aluminum alloy was joined to a 304 stainless steel by friction welding. The structure of aluminum alloy was refined in the vicinity of the weld interface. However, the Vickers hardness was decreased near the interface since the precipitates were dissolved in the aluminum alloy matrix by the friction heat. The width of heat affected zone (HAZ) was decreased as the increase in the friction and upset pressure (P1 and P2) increased. The sound joints were obtained welded by P1 =30 MPa, P2 =60 MPa and t1 (friction time) ≥2.0 s. The higher P1 made the joint strength decrease owing to the excess formation of brittle intermetallic compounds at the weld interface. The inter-diffusion of each element through the weld interface were revealed using TEM–EDS analysis. Fe2Al5 was mainly formed at the weld interface. The welding temperature was estimated to be under the eutectic temperature of Al/Fe system(925 K) by the thickness of intermetallic compound. Therefore, it is assumed that this friction welding was carried out in solid state in this system.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.