Al‐0.1%Sn‐Fe合金の電気化学的性質と腐食挙動
スポンサーリンク
概要
- 論文の詳細を見る
The effect of iron content and cooling rate after brazing heat treatment on the electrochemical property and the corrosion behavior of Al–0.1 mass%Sn–Fe alloys were investigated. Pitting potential abruptly became noble at the critical iron content which decreased with the decrease of cooling rate. Tin is preferentially precipitated around Al–Fe intermetalic compounds. As the pitting of matrix initiated at the precipitates, the corrosion behavior depended on distribution of them. As the corrosion of the Al–0.1 mass%Sn–0.5 mass%Fe alloy with slower cooled after brazing heat treatment was a sort of uniform type consisting of a great many small pits, application of the alloy as a pitting corrosion resistant one can be expected.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.