アルミニウム鋳造の最新技術 結晶微細化した亜共晶Al‐Si‐Cu合金の半溶融加圧鋳造組織と機械的性質
スポンサーリンク
概要
- 論文の詳細を見る
Change in the morphology of dendrite primary crystals heated at a temperature of solidification range was examined in hypoeutectic Al–Si–Cu alloys. Dendritic α–Al crystals, which have been refined by the addition of grain refiner, Ti–B and cast into copper mold with the cooling rate more than 10 K/s, are easily spheroidized only by heating to semi-solid state. The size of spheroidized α–Al phases is about 100 μm in diameter under the semi-solid state of fraction solid 0.4 at 860 K. This morphology of α–Al crystals is suitable for the semi-solid squeeze casting. Semi-solid squeeze cast Al–7% Si–3%Cu alloys containing 0.1~1.0%Fe have superior in tensile properties, especially in elongation. The elongation of an as-cast alloy containing 1%Fe is 9%. The tensile properties of semi-solid squeeze cast alloys are further improved by solution heat treatment.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.