準結晶を含むガス噴霧Al‐7.8%V‐4%Fe合金粉末の押出成形と耐熱強度
スポンサーリンク
概要
- 論文の詳細を見る
The bulk material with a size of about φ8 mm × 300 mm was produced by extrusion of gas atomized Al–7.8 mass%V–4 mass%Fe alloy powder at 623, 673 and 723 K. The gas atomized powder consists of icosahedral, fcc–Al and Al11V phases and has a spherical shape with an average diameter of about 31 μm. The bulk material extruded at 623 K consists of icosahedral and Al phases and has a high packing density of approximately 100%. The ultimate tensile strength (σUTS), plastic elongation (εP), Vickers hardness (HV) and Young's modulus (E) at room temperature are 585 MPa, 4.5%, 190 and 84.8 GPa, respectively. And then the σUTS, εP and HV at 573 K are 305 MPa, 5.0% and 90, respectively. The HV remains unchanged even after holding for 432 ks at 573 K. The coefficient of thermal expansion is 21.4 × 10−6K−1, which is smaller by 15% than that of the 7075–T6 alloy. The bulk materials extruded at 673 and 723 K also have the similar high elevated temperature strength of 291 and 277 MPa, respectively, at the temperature 573 K. The extruded bulk materials with high elevated-temperature strength are expected to develop as a new type of high strength material.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.