クロム酸イオンと酸化物粉体添加によるアルミニウム交流電解皮膜の硬質化
スポンサーリンク
概要
- 論文の詳細を見る
Physical properties and compositions of hard coatings formed by AC process were investigated in comparison with those by DC process. Electrolysis was carried out at current density 3 A/dm2 and at bath temperature 10-20°C, using a sulfuric acid solution containing chromic acid ion (potassium dichromate, chrome (VI) oxides and oxide powders (aluminum oxide, glass beads). Addition of both potassium dichromate and glass beads provided the best properties in hardness for the AC process films by their combined effects, while the hardness and abrasion properties were improved by the addition of chromic acid ion and oxide powders. These characteristic features are thought to result from an increase in aluminum content in the film by the addition of chromic acid, and also from the levelling of the film surface caused by the addition of oxide powders. But AC process films generally showed lower hardness than DC process films. It is considered, on the basis of AAS, EPMA and SIMS analyses, that this lower hardness is attributable to a smaller amount of aluminum oxide contained in AC process films.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.