Al‐6%Mg合金の結晶粒成長挙動
スポンサーリンク
概要
- 論文の詳細を見る
Grain growth behavior in Al–6%Mg alloy was investigated and the results were as follows. (1) The grain growth kinetics for the early stages of annealing obeyed parabolic kinetics (D/2)2 − (D0/2)2=Kt, where D is a grain size after annealing for time, t, K is a temperature-dependent rate parameter and D0 is the grain size at time equal to zero. The apparent activation energy of the grain growth for the early stages of annealing was 1.05 eV and it was supposed that the process was diffusion controlled by Mg atoms. Equilibrium grain size was present for the later stages of annealing and the temperature dependence was observed. (2) It is supposed that the equilibrium grain size is caused by the loss of mobility due to the segregation of solute atom (Mg) on the grain boundary, and that its temperature dependence is due to the temperature dependence of the magnitude of segregation of solute atom on the grain boundary.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.