リサイクルと環境問題を考える 6061アルミニウム合金の組織および諸特性に及ぼす残留バナジウムの影響
スポンサーリンク
概要
- 論文の詳細を見る
Vanadium is a useful element for the removal of silicon from the recycled aluminum melt by filtering since it reacts with silicon and forms giant intermetallic compounds. In such a procedure, vanadium may remain in the melt, but its influence on various properties of aluminum alloys has not been made clear. This study was conducted for the purpose of clarifying the influence of the remained vanadium on various properties of 6061 aluminum alloy from a view point of metallography. V2Mg3Al18, Al3V, Al–Si–V–Mg and V2Mg3Al18 compounds are crystallized by a vanadium addition to 6061 aluminum alloy. Peak hardness of the alloy with 2.79%V is lowered because both silicon and magnesium are contained in the compounds. Tensile strength and proof strength of the alloy containing vanadium more than 0.46% gradually decrease up to the vanadium content of 1.33%, at which the largest peak hardness appears, and remarkably decrease in the range over 1.33%V as vanadium content increases. Ductility, toughness and formability are largely degraded with an increase ofvanadium content. This is caused by a fact that larger amount of coarse compounds crystallize as vanadium content is higher. Consequently, it is required that vanadium content in the 6061 alloy is less than 0.2% to guarantee the elongation satisfying the JIS value.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.