Improvement of the oxidation resistance of a 5th generation nickel-base single crystal (SC) superalloy through the addition of silicon was attempted. A 5th generation nickel-base SC superalloy TMS-173 (5.6Co-2.8Cr-2.8Mo-5.6W-5.6Al-5.6Ta-0.1Hf-6.9Re-5.0Ru (Ni-bal. mass%)) has excellent creep properties. This was accomplished by increasing the ruthenium content to accommodate the increased amount of rhenium, an element that improves high temperature properties. On the other hand, their additions decrease oxidation resistance. In this study, silicon was added to modify the oxidation property. However, TMS-173 alloy contains saturated amounts of solution strengthening elements in γ/γ′; therefore, in order to add silicon, tantalum was substituted out to maintain γ/γ′ microstructure. A 50-Cycle oxidation test at 1100°C was carried out to evaluate the effects of silicon, with each cycle lasting one hour. SEM and EDX were used for cross-section analysis. TMS-173-Ta+Si (5.8Co-2.9Cr-2.9Mo-5.8W-5.8Al-0.1Hf-7.2Re-5.2Ru-1.9Si (Ni-bal. mass%)), showed excellent oxidation resistance; weight loss was much less than that of Rene'N5, and the oxide layer formed was exclusively Al2O3.
- The Japan Institute of Metals and Materialsの論文
The Japan Institute of Metals and Materials | 論文
- Control of Ferromagnetism in Magnetic Semiconductors and Application for Spin-polarized Electron Source
- 超高純度金属の実用化への道
- 非極性 GaN 層中の微結晶粒の効率的な検出と今後の展望
- Recycling Technology for Platinum Group Metals by Using Perovskite-type Oxides
- Specimen Preparation Methods with FIB for In-Situ TEM Observations in Materials Science—TEM Specimen Preparation by FIB with Glass Manipulator—