定電流電解重合によるZn上へのポリ2-ビニルピリジン膜の形成
スポンサーリンク
概要
- 論文の詳細を見る
Poly(2-vinylpyridine) films were deposited on Zn substrate by electropolymerization using galvanostatic technique at 30°C in pH 5 aqueous solution containing methanol. Films were also formed by employing cyclic voltammetry and potentiostatic techniques; these were compared with those formed using galvanostatic electrolysis. The thickness of films formed by galvanostatic electrolysis increased in proportion to the amount of charge passed during electropolymerization but decreased with increasing current density because of increased hydrogen evolution. The FT-IR spectra and the color of the films suggested that the structure of poly(2-vinylpyridine) films changed from the non-branched to the branched chain type with the higher current densities. The anodic current density for Zn dissolution in 3%NaCl solution was significantly decreased by coating with poly(2-vinylpyridine) films. After electropolymerization at 50 A•m-2, the anodic reaction was most inhibited, showing excellent corrosion resistance. Although the electrochemical techniques employed for the film preparation had no influence on the thickness or the structure of films, the films formed by galvanostatic electrolysis contained the fewest cracks and gave the best corrosion resistance.
- The Japan Institute of Metals and Materialsの論文
The Japan Institute of Metals and Materials | 論文
- Control of Ferromagnetism in Magnetic Semiconductors and Application for Spin-polarized Electron Source
- 超高純度金属の実用化への道
- 非極性 GaN 層中の微結晶粒の効率的な検出と今後の展望
- Recycling Technology for Platinum Group Metals by Using Perovskite-type Oxides
- Specimen Preparation Methods with FIB for In-Situ TEM Observations in Materials Science—TEM Specimen Preparation by FIB with Glass Manipulator—