Phase Relationship for the CaO–SiO2–FeO–5 mass%P2O5 System with Oxygen Partial Pressure of 10−8 atm at 1673 and 1623 K
スポンサーリンク
概要
- 論文の詳細を見る
Dephosphorization process by using multiphase flux requires smaller slag amount than conventional process, while the high refining efficiency can still be achieved, due to the promotion of the CaO utilization. In order to provide proper phase diagram for understanding the reaction mechanism, the phase relationship for the CaO–SiO2–FeO–5 mass%P2O5 quaternary system has been studied with oxygen partial pressure of 10−8 atm at 1673 and 1623 K by using chemical equilibration technique. It has been found that the solid solution exists only as 2CaO·SiO2–3CaO·P2O5, and the ratio between both varies with liquid phase compositions. On the other hand, the liquidus for both 1673 and 1623 K that saturated with above solid solution, moves close to the FeO apex comparing with the CaO–SiO2–FeOx system equilibrated with iron. Besides, the large phosphorus partition ratio between solid solution and liquid slag has also been found, which agrees well with previous works. Based on the regular solution model, both activities and activity coefficients of P2O5 have been discussed.
- The Japan Institute of Metals and Materialsの論文
The Japan Institute of Metals and Materials | 論文
- Control of Ferromagnetism in Magnetic Semiconductors and Application for Spin-polarized Electron Source
- 超高純度金属の実用化への道
- 非極性 GaN 層中の微結晶粒の効率的な検出と今後の展望
- Recycling Technology for Platinum Group Metals by Using Perovskite-type Oxides
- Specimen Preparation Methods with FIB for In-Situ TEM Observations in Materials Science—TEM Specimen Preparation by FIB with Glass Manipulator—