Dense P/M Component Produced by Solid Freeform Fabrication (SFF)
スポンサーリンク
概要
- 論文の詳細を見る
Using fine metal powders, we were able to fabricate dense P/M (powder metallurgy) products by a three-dimensional inkjet printing system. We used carbonyl nickel powder with a mean particle size of 5 μm as a raw material and examined two binder supply methods: (i) supplying a binder directly from the inkjet head (DB method), and (ii) coating the powder with a water-soluble polymer and then supplying thin polymer-dissolved water from the inkjet head (CB method). The layered green product was sintered in a hydrogen atmosphere at a temperature in the range of 1073–1623 K. Sintered samples fabricated by the CB method had non-uniform microstructure due to agglomeration of the coated powder. In samples made by the DB method, the macroscopic shape was retained after high-temperature sintering at 1623 K, and a high density of over 90% was achieved, which was attributed to uniform powder cohesion in the laminating process.
- The Japan Institute of Metals and Materialsの論文
The Japan Institute of Metals and Materials | 論文
- Control of Ferromagnetism in Magnetic Semiconductors and Application for Spin-polarized Electron Source
- 超高純度金属の実用化への道
- 非極性 GaN 層中の微結晶粒の効率的な検出と今後の展望
- Recycling Technology for Platinum Group Metals by Using Perovskite-type Oxides
- Specimen Preparation Methods with FIB for In-Situ TEM Observations in Materials Science—TEM Specimen Preparation by FIB with Glass Manipulator—