Optimization of Hot Rolling Process of Gravity Cast AZ31-xCa (x=0-2.0 mass%) Alloys
スポンサーリンク
概要
- 論文の詳細を見る
In this study, the effects of Ca content and processing variables on the external surfaces and tensile properties of hot-rolled AZ31-xCa sheets were evaluated systematically. The number and length of side crack were decreased with increasing preheating temperature and decreasing reduction ratio per pass and Ca content. The UTS and YS were not strongly dependent on the Ca content but the elongation decrease with increasing Ca content. The amount of decrease in elongation due to increase in Ca content was least when the sheets were fabricated under preheating temperature of 400°C and reduction ratio per pass of 15%. The sheets had the sound external features with little side cracks by homogenization of gravity cast AZ31-xCa alloys before hot rolling. In the cases of AZ31-xCa alloys containing under 1 mass% Ca, the annealed sheets after homogenization and hot rolling had the similar tensile properties to those of AZ31 sheet.
- The Japan Institute of Metals and Materialsの論文
The Japan Institute of Metals and Materials | 論文
- Control of Ferromagnetism in Magnetic Semiconductors and Application for Spin-polarized Electron Source
- 超高純度金属の実用化への道
- 非極性 GaN 層中の微結晶粒の効率的な検出と今後の展望
- Recycling Technology for Platinum Group Metals by Using Perovskite-type Oxides
- Specimen Preparation Methods with FIB for In-Situ TEM Observations in Materials Science—TEM Specimen Preparation by FIB with Glass Manipulator—