Microstructure and Magnetic Properties for Highly Coercive FePt Sputtered Films
スポンサーリンク
概要
- 論文の詳細を見る
In this paper, we review our recent investigations on the magnetic properties and microstructure of highly coercive FePt films prepared on both MgO (001) and MgO (110) substrates with various film thicknesses (<I>t</I><SUB>N</SUB>). Perpendicularly magnetized FePt (001) film were obtained on MgO (001) substrates, while FePt (101) films with the easy magnetization axis canted from the perpendicular direction to the film plane were obtained on MgO (110) substrates. The film morphology changes from a particulate to a continuous state depending on <I>t</I><SUB>N</SUB>. A drastic decrease in the coercivity has been observed with the percolation of particles for FePt (001) films, when <I>t</I><SUB>N</SUB> exceeds a critical thickness, <I>t</I><SUB>c</SUB>=45 nm. On the other hand, the gradual decrease of <I>H</I><SUB>c</SUB> with <I>t</I><SUB>N</SUB> has been observed in FePt (101) films and no remarkable change is seen at the critical thickness where the film morphology changes from a particulate to continuous state.
- The Japan Institute of Metals and Materialsの論文
The Japan Institute of Metals and Materials | 論文
- Control of Ferromagnetism in Magnetic Semiconductors and Application for Spin-polarized Electron Source
- 超高純度金属の実用化への道
- 非極性 GaN 層中の微結晶粒の効率的な検出と今後の展望
- Recycling Technology for Platinum Group Metals by Using Perovskite-type Oxides
- Specimen Preparation Methods with FIB for In-Situ TEM Observations in Materials Science—TEM Specimen Preparation by FIB with Glass Manipulator—