Chemical Modification of Solid Surfaces at Nano-level by Water Cluster Ion Irradiation
スポンサーリンク
概要
- 論文の詳細を見る
We have investigated impact-process of water cluster ions on solid surfaces. Various kinds of substrates such as Si(100), SiO2 and PMMA substrates were irradiated by adjusting the acceleration voltage and the ion dose. The sputtered depth of these substrates increased with increase of the acceleration voltage, and it was 37 nm for Si, 49 nm for SiO2, and 2.9 μm for PMMA substrates, respectively at an acceleration voltage of 9 kV and an ion dose of 1.0× 1016 ions/cm2. The sputtering yield calculated was 19 atoms per ion for Si and 13 molecules per ion for SiO2, which was approximately ten times larger than that for Ar monomer ion irradiation. The XPS measurement showed that the Si substrate surfaces sputtered at an ion dose of 1.0× 1016 ions/cm2 had an oxide layer such as SiOx. The oxide layer thickness increased with increase of the acceleration voltage, and it was approximately 10 nm at an acceleration voltage of 6 kV. On the other hand, at lower ion doses such as 1.0× 1014 ions/cm2, the ratio of the sputtered depth of Si surface to SiO2 surface became approximately 10. This indicated that the chemical erosion such as silicon hydride occurred, resulting in enhancement of chemical sputtering of Si substrates. Furthermore, for the case of PMMA substrates, the chemical erosion of the substrate surfaces occurred probably through the exchange between CH3 and H radicals, and the chemical sputtering by the ejection of methacrylic acid molecule was enhanced. The surface roughness of PMMA substrates irradiated was less than 2 nm, and the smooth surface at the nano-level was obtained. In addition, micro-patterning was demonstrated with the water cluster ion beams on the PMMA substrates. [DOI: 10.1380/ejssnt.2011.163]
- 公益社団法人 日本表面科学会の論文
公益社団法人 日本表面科学会 | 論文
- An XPS Analysis of the Interfacial Interaction between Oxides and Epoxy Resin.
- A Structure Analysis of Langmuir-Blodgett Magnetic Films by X-ray Diffraction.
- Structure and Reactivity of Surface Compounds Formed on Single Crystal Metal Surfaces During Catalytic Reactions.
- Atomic-Layer Etching of Si by Low Energy Ion Irradiation.
- Microstructure Observations of (Nd, Ce)2CuO4 Superconducting Thin Films by Using Cross-Sectional HRTEM and the Mechanism f Film Growth.