Effect of alumina particle size on aging in Al2O3/Al-Cu-Mg composite materials.
スポンサーリンク
概要
- 論文の詳細を見る
Effect of particle size on aging in alumina particle dispersed composite materials has been investigated by transmission electron microscopy. Age-hardening curves of composite materials containing larger alumina particles ranging from 8 to 15μm, were quite similar to those of mother alloy. In these composites, aging processes started with the formation of GPB zones and were followed by the precipitation of S' intermediate phases. While in the composite materials containing smaller alumina particles ranging from 1 to 3μm, the hardness under peak aging condition was lower than that of mother alloy. The electrical resistivity just after solid solution treatment had also lower values than that of mother alloy. Their aging processes started with the formation of GP zones and were followed by the precipitation of θ' intermediate phases. The dissimilarity of these aging processes depending on size of alumina particles caused by the decrease of magnesium content in the matrix due to the formation of spinels on alumina particles.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.