Spontaneous infiltration velocity in fabrication process of particulate reinforced magnesium composites.
スポンサーリンク
概要
- 論文の詳細を見る
The fabrication of magnesium matrix composites using spontaneous infiltration phenomenon becomes possible by adding SiO2 powder (infiltration agent) to SiCp powder (reinforcement), even at relatively low holding temperature and under argon atmosphere. It is probably because the wettability between Mg melt at the infiltration front and reinforcement is improved by Mg/SiO2 thermit reaction heating. In this paper, the infiltration velocity is measured. Especially the effects of SiCp diameter from 2 to 8μm and SiO2 content are discussed. The results show that the infiltration velocity is in the range from 0.01 to 0.7mm•s-1, and it depends both on SiCp diameter and on SiO2 content. The effect of SiO2 content on infiltration velocity is complex, i. e. the velocity increases with increasing SiO2 content up to 15mass%, and then decreases steeply. This decrease is probably caused by the increased infiltration resistance with MgO and Mg2Si, products of Mg/SiO2 reaction. Up to 15mass%SiO2, the increasing of infiltration front temperature by increasing SiO2 content is efficient, resulting in faster infiltration velocity. Above this content, the effect of infiltration resistance by the reaction products becomes more significant than that of the temperature increase, resulting in slower velocity.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.