インサ-トメタルを用いた6061アルミニウム合金とS45C炭素鋼の摩擦圧接
スポンサーリンク
概要
- 論文の詳細を見る
Friction welding of a 6061 aluminum alloy to a S45C carbon steel was carried out using the insert metal of a 1050 aluminum. Optimum thickness of the insert metal, friction pressure, forge pressure, friction time and rotational speed of welding conditions were determined as 4mm, 90MPa, 300MPa, 1.2s and 2250rpm, respectively. When the insert metal turned into a thin (20-30μm) and homogeneous layer at the weld interface, the maximum joint efficiency of tensile strength was obtained and was about 95%. Successful welds were obtained by taking each optimum welding condition even if the thickness of the insert metal was varied from 2 to 6mm.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.