A forming roll was introduced in a conventional melt spinning process to improve free solidified surface of the strip. Effect of the forming roll was tested at the condition as below. Roll speed ranges from 2 to 12m/s. Roll gap is 0.2mm. Slit size is 0.8 × 20mm. Ejection gas pressure is 20kPa. Distance between nozzle and forming roll ranges from 40 to 160mm. Forming load is 98N. Specimen is Al-12 mass%Si alloy. Roll speed and nozzle-forming roll distance are the most important factors in this process. Because they affect the solidification on the free solidified surface. The flatness and microstructure of the strip can be made sound by the modified process of this study.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.