Aging behavior of Al-4.5%Mg, Al-4.5%Mg-0.35%Mn and Al-1.3%Mg-1.1%Mn alloys containing 0.2%Cu.
スポンサーリンク
概要
- 論文の詳細を見る
Aging behavior of solution-treated and cold-rolled Al-4.5%Mg, Al-4.5%Mg-0.35%Mn and Al-1.3%Mg-1.1%Mn alloy sheets containing 0.2%Cu was investigated by tensile test and electron microscopy. The alloy samples were isochronally aged at temperatures between room temperature and 300°C for 20s or isothermally aged at 220°C for 5 to 18000s. The decrease in the mechanical strength at higher temperatures than 260°C or at prolonged aging time longer than 1200s is suppressed by reducing the amount of Mn addition and increasing homogenization temperature as well as solidification rate during casting. The increased volume fraction of fine Mn-baded dispersoids is found to have the effect to decrease the mechanical strength during aging. The heterogeneous precipitation of the S phase (Al2CuMg) on the fine Mn-based dispersoide is found to occur in the solution-treated and then cold-rolled Al-1.3%Mg-1.1%Mn-0.45%Cu alloy sheet aged at 240°C for 2h.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.