Influence of Al addition on electrical resistivity and phase constitution in quenched Ti-20 mass%V alloy.
スポンサーリンク
概要
- 論文の詳細を見る
Electrical resistivity anomalies in β type Ti alloys including negative temperature dependence were previously interpreted by fully reversible formation and disappearance of athermal ω phase with cooling and heating. In the present work, influence of Al addition up to 10mass% on some properties of Ti-20%V alloy in as quenched state from β region were investigated. Resistivity increases with concentration of solute Al. Addition of 3%Al changes the temperature-resistivity curve of Ti-20%V alloy, which had a resistivity maximum between 77K and room temperature, to the curve having negative temperature coefficient in whole of the above temperature range. In alloys below 5%Al, hardness decreases slightly with Al addition, namely no solid solution hardening by Al can be observed. However, the hardening appears above 8%Al clearly. These results suggest that the starting, perhaps also finishing, temperature of athermal ω phase formation is lowered and that the amount of athermal ω phase at room temperature is decreased by the Al addition. This interpretation is qualitatively confirmed by electron diffraction.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.