Zn-22%Al合金板の超塑性変形挙動の解析
スポンサーリンク
概要
- 論文の詳細を見る
Superplastic deformation behaviours in superplastic Zn-22%Al eutectoid alloy were investigated. Smooth and notched specimens having the thickness of 1, 2 and 3mm were applied in the present experiment in view points of the change of true strain rate and m values during the course of the tensile superplastic deformation and variation of the fracture elongations. The results are summarized as follows: (1) Superplastic deformation of the smooth specimens was reasonably explained by dividing the deformation into sequential five steps. (2) Superplastic deformation of the notched specimens was reasonably explained by dividing the deformation into sequential two steps without passing the first three steps observed in case the smooth specimens. (3) Fracture elongations of the smooth specimens were effected by the variation of the specimen thickness and increased by 12 to 25% with the increase of the specimen thickness from 1 to 3mm. (4) The fracture elongation of the notched specimens was also effected by the specimen thickness and increased by 2 to 20% with the increase of the thickness of the notched specimen.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.