Curling behavior during aluminum tube end flaring with hemispherical dies.
スポンサーリンク
概要
- 論文の詳細を見る
The curling behavior in aluminun was investigated to clarify the condition for curling during the tube end spherical flaring. The influence of die radius R, lubricant, ratio of the tube wall thickness to diameter t0/d0, work hardening exponent n and forming speed V on the condition for curling was investigated in the aluminum tubes. It was found that the curling took place when the apparent die angle α' at the initial contact point of a tubular specimen to the hemispherical die was larger than the critical die angle αS with the conical die. Furthermore, the multi- and single-stage methods to prevent the curling in the case of the conical die were proposed and experimentally examined. The curling mode was prevented under the proposed preventing condition. Thus, these results suggested that the curling mechanism in the hemispherical die was similar to that in the conical die.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.