Al-Li-Cu-Mg-Zr合金の超塑性挙動 (Al-Li系合金特集号)
スポンサーリンク
概要
- 論文の詳細を見る
Superplastic behaviors of an Al-Li-Cu-Mg-Zr alloy for aerospace application have been investigated over the temperature range 600-800K and the initial strain rate range 1×10-4-1×10-2s-1. In cold-rolled and annealed sheet specimens having fine and equiaxed grains of about 5μm diameter, superplasticity was observed above 725K, wherein the maximum elongation of 480% appeared and the strain rate sensitivity was determined to be 0.45 at 800K. As-rolled sheet specimens became much more superplastic than annealed ones, when holding time prior to the tensile test was chosen appropriately. No improvement in ductility was found in the temperature increasing tensile tests. Extruded specimens having fine but elongated grain structure did hot show superplasticity at all, probably because grain boundary sliding was suppressed due to a geometrical reason.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.