炭素被覆アルミナの塩素化における塩化アルミニウム粉体の製造
スポンサーリンク
概要
- 論文の詳細を見る
condensation behaviors of gaseous aluminum chloride were examined on the bases of such factors as flowing velocity of gaseous aluminum chloride into a condenser, velocity of fluidizing gas into the condenser and temperature distribution in the condenser. Aluminum chloride power is continuously recovered with prolonged time at a rate about 0.15 to 0.18 g/mn. The effective recovery of aluminum chloride powder is increased about 25% by adding solid aluminum powder into the condenser. The optimum conditions for producing aluminum chloride powder are achieved by simultaneous control of the flowing velocity of gaseous aluminum chloride and the velocity of fluidizing gas into the condenser. If the former is faster than the latter, gaseous aluminum chloride adheres to the condenser wall. The characteristics of aluminum chloride powder recovered are; average diameter about 74 μm, apparent specific gravity 0.64 g/cm3 and angle of repose about 41°.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.