The structural changes in 3004 base alloys with commercial composition and higher Si or Mg content have been investigated by mainly optical microscopic observation and X-ray diffraction method. Heating led to the transformation of the coarse primary phase Al6 (Fe, Mn) into the equlibrium phase α-Al12 (Fe, Mn)3Si; so-called α transformation. TTT diagrams showed the C-curves having a nose near at 550°C. The activation energy for α transformation was estimated to be about 2.6eV. It suggests that the rate controlling process of α transformation is the diffusion of Mn atoms in Al matrix. In higher Si containing alloy, α transformation was accelerated, while, in higher Mg containing alloy, it was remarkably suppressed. The above results can be attributed to the differense of effective Si content for α transformation.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.