氷晶石浴へのアルミナの溶解機構
スポンサーリンク
概要
- 論文の詳細を見る
It is of great importance to understand the mechanism and the rate of Al2O3 dissolution into cryolite melt. This study is mainly concerned with the direct observation of melt through microscope and mesuring the dissolution rate of various type of Al2O3 by using the hot-thermo couple technige. The experimental results indicated that the dissolution pattern of Al2O3 in cryolite melt is divided into three types due to difference in crystal form irrespective of shape and size of Al2O3 and mode of press. The dissolution pattern of θ, δ and κ-alumina obtained by calcination of boehmite and gibbsite at low temperature showed type I and these dissolution proceeded rapidly from top part of Al2O3 into melt. On the other hand, the dissolution rate of Al2O3 obtained from gibbsite was very small and showed type II or III. Such classification was dependent upon the content of α-alumina expressed by relative X-ray intensity of α-alumina in the calcined products. The effect of addition of other fluorides to the cryolite melt upon the dissolution rate has been also investigated. The addition of NaF was found effective to increase the dissolution rate of alumina.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.