Rolling and annealing textures of 99.99% aluminum hot rolled at 480° to 590°C, cold rolled by 98.6% and annealed for 1h at 400°C were investigated. They depend on hot rolling temperature; the lower the hot rolling temperature the stronger is S-orientation in rolling texture, while the higher the hot rolling temperature, the stronger is cube orientation after annealing. A traceable amount of (100) nuclei still remain in aluminum hot rolled at elevated temperatures even after heavy reduction cold rolling and grow up to primary recrystallizing origins developing the cube texture.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.