Al-Mg-Fe-Si合金連続鋳造塊の樅の木組織
スポンサーリンク
概要
- 論文の詳細を見る
Formation of the fir-tree structure in DC cast 5005 alloy was studied by means of Xray-diffraction and optical microscopy comparing with that of Al-Fe-Si alloy (1100). Unidirectional solidification experiments and direct measurements of cooling rate during solidification in DC casting process were also made. The main intermetallic compounds in the outer and inner regions of fir-tree structure in DC cast 1100 alloy are respectively Al3Fe and Al6Fe as shown in the previous works. The major phase AlmFe is found in the outer region in 5005 alloy and Al6Fe and Al3Fe in the inner region. A clearly shaded boundary lies between AlmFe and Al6Fe (or Al6Fe + Al3Fe) phase regions in the ingot of each alloy unidirectionally solidified. The cooling rate at the boundary(the minimum cooling rate for AlmFe formation, Vc) in 5005 alloy is smaller than those in Al-0.5%Fe and 1100 alloys, and is in the range of cooling rate in DC castings. The fir-tree structure of AlmFe is formed when cooling rate near the surface of DC cast 5005 alloy exceeds Vc.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.