Al-8%Mg合金の応力腐食割れに及ぼす水素の影響
スポンサーリンク
概要
- 論文の詳細を見る
The mechanism for stress corrosion in the Al-Mg alloy is investigated. Charged hydrogen has an influence to the susceptibility to stress corrosion and lowers the life. The upper and lower critical concentrations are found. Increase in the susceptibility is saturated beyond the former at the amount of hydrogen increase 0.35 cc/100g and the susceptibility is unchanged below the latter at 0.15 cc/100g. The amount of hydrogen absorbed in the alloy exceeds the latter even in the normal stress corrosion condition. The stress corrosion cracking proceeds through the following stages. i) Electrochemical pitting ii) A strong acid atmosphere constituted near the bottom of the pitts by impediment in fluidity of corrosive mediums leads to a continuous reaction accompanying hydrogen generation iii) A part of generated hydrogen absorbed and concentrated in grain boundaries results in formation of embrittle paths iv) Cracks nucreate when a concentrated stress exceeds a fracture strength of embrittled region, and stop by stress relaxation caused by crack opening or by reaching to an unembrittled region. And v) the stages above mentioned are repeated.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.