PbCl2-CdCl2系蒸気のクヌ-セン・セル-マスフィルタによる熱力学的研究
スポンサーリンク
概要
- 論文の詳細を見る
Mass spectrometric analysis of the vapor phase of PbCl2-CdCl2 molten salt mixture was performed as a preceeding test for measuring AlCl3 in a molten salt system from the view point of aluminum smelting. The vapor species over CdCl2 and PbCl2 are Cd2Cl4(g) and CdCl2(g), and PbCl2(g) respectively. No heavier species are detected up to 970K. The heat of sublimation and the activities of PbCl2 and CdCl2 were measured over the whole composition range. The PbCl2-CdCl2 melt can be regarded as an ideal solution because of a slightly negative deviation from Raoult's law at 909K. This system is found to be different from the melts of PbCl2 or CdCl2 with alkali chlorides. The activity results are in good agreement with the physicochemical measurements on this system. A CdCl2-Cd metal system was also massspectrometrically examined. The inexpensive mass-filter system will be useful for studying the molten salt systems.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.