急冷凝固したAl-Zr合金の組織と相分解
スポンサーリンク
概要
- 論文の詳細を見る
Solidified structure, mechanical properties and phase decomposition were investigated on the Al-(0.23.4)%Zr alloys chill-cast or splat quenched to extend the solid solubility of Zr in Al. Slowly cooled alloys containing 1.13.4%Zr have a equilibrium Al3Zr phase in the shape of a large needle. Chill-cast alloys containing 0.2 to 1.4%Zr have f.c.c. solid solutions highly supersaturated. Chill-cast alloys containing Zr more than 1.7% have a non-equilibrium Ll2 structure. The metastable Al3Zr plays active nuclei for the angular structure and leads to grain refining. Presence of the anglar structure containing more of Zr results in abrupt increase of strength of the alloys. Decomposition of the supersaturated solid solution during tempering occurs by forming a spherical intermediate cubic Al3Zr phase. The spherical precipitate is very slowly coarsened and then preferentially grows along the definite matrix direction. The grain boundary reaction is also observed in the early stage of againg. These precipitates are metastable Al3Zr of Ll2 type structure which is stable during prolonged aging time.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.