極低温におけるアルミニウム合金の疲労
スポンサーリンク
概要
- 論文の詳細を見る
Rotation bending fatigue tests at room and liquid nitrogen temperatures were carried out on 2024-T4, 5056-H32 and 1050-H18 alloys. The fatigue strength is much greater at the liquid nitrogen temperature than at room temperature. Both the ratio of the fatigue strength at the liquid nitrogen temperature to that at room temperature and the ratio of fatigue strength to ultimate strength of 5056-H32 alloy are greater than those of 2024-T4 alloy. The fatigue strength of 5056-H32 alloy at the liquid nitrogen temperature is nearly equal to that of 2024-T4 alloy. Therefore, when the fatigue strength at cryogenic temperature is significant, 5056-H32 having excellent weldability would be more favorable than 2024-T4 alloy.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.