5083合金の熱間加工性に及ぼす加工前均質化熱処理条件の影響
スポンサーリンク
概要
- 論文の詳細を見る
Hot torsion tests were conducted on the 5083 aluminum alloy having cast structure under the conditions of shear strain rate range from 0.1 to 75 sec-1 and temperature range from 400°C to 500°C. The two stages solution treated materials are superior in hot workability than one stage treated ones. It is possible by electron microprobe analyses to deduce the composition and relative amount of constituent elements of the precipitated intermetallic compounds which decrease the ductility of the alloy. These intermetallic compounds are composed of such elements as Fe, Mn, Cr and Si.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.