過共晶Al-Si合金の切削における工具逃げ面摩耗部の付着物について
スポンサーリンク
概要
- 論文の詳細を見る
In machining the hyper eutectic Al-Si alloy, the severe flank wear and the considerable deposit on the flank wear land of the tool are observed. This report deals with the deposit produced under several cutting conditions by EPMA to study the relation between the flank wear and the deposit.The following results were obtained.(1) The composition of the deposit on cutting edge side of the flank wear land was nearly the same as the work material, and silicon was principally adhered on the wear limit side.(2) The distribution of aluminum and silicon, which are the main elements of the deposit, was related to the width of the flank wear almost independently of cutting tool materials, cutting oils, cutting speeds, etc.(3) The primary silicon crystal in the deposit is crushed by abrasive action when it passes through the flank wear surface.(4) It seems that the influence of silicon deposit on the growth of the flank wear was nearly the same as that of aluminum deposit in dry cutting, but the former was less influencial than the latter in wet cutting.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.