Effects of small amounts of additional elements on stress corrosion cracking of Al-Zn-Mg alloys:Studies on stress corrosion cracking of Al-Zn-Mg alloys (6th report)
スポンサーリンク
概要
- 論文の詳細を見る
Stress corrosion cracking tests were performed on Al-4.5wt.%Zn-2.9wt.%Mg alloy and the same alloy containing an additional element of about 0.1at.% of any one of Cu, Cr, Ti and Zr. In addition, metallurgical parameters assumed to have effects on stress corrosion cracking sensitivity of the alloys were determined.The results obtained were summarized as follows:(1) There were no parameters having a close relationship to stress corrosion cracking sensitivity of the alloys. Though there were great differences in metallurgical properties between the alloy containing copper and the alloy containing any one of Cr, Ti and Zr, any of these elements improved stress corrosion resistance of the alloys. These phenomena made us to suppose that the stress corrosion cracking sensitivity of the alloys would be attributed to a complicated composition of many factors.(2)Al-4.5wt%Zn-2.9wt.%Mg alloy aged at 90°C for 30hrs. had greater toughness and some of their properties were more sensitive to corrosion circumstances as compared with the alloy subjected to two-stepped aging. The alloy containing copper had poorer toughness and its decrease of strength in a corrosive agent was greater, but its corrosion resistance was higher. The properties of the alloy containing any one of Cr, Ti and Zr were nearly inverse to those of the alloy containing copper.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.