Serrated yielding in Al-Zn alloys
スポンサーリンク
概要
- 論文の詳細を見る
Serrated yielding was observed in quenched Al single crystals and quenched dilute Al-Zn single crystals, which had been deformed by tension at room temperature.The characteristics of serrated yielding of these crystals were investigated by its dependence on quenching temperature, tempering temperature, and strain rate, and appearance of slip lines.The principal results obtained were as follows:(1) The serrated yielding was observed only in single crystals containing Frank-sessile dislocation loops as secondary lattice defects.(2) The dependence of the serrated yielding on quenching and tempering temperatures would by attributed to sizes and densities of the Frank-sessile dislocation loops.(3) The dependence of the yielding on strain rate would be attributed to the interaction between moving dislocations and Frank-sessile dislocation loops.(4) It would be concluded from these experiments that the serrated yielding may be controlled by superjogs formed by the interaction between the moving dislocations and the Frank-sessile dislocation loops.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.