Residual stress in butt welded 5083 aluminum alloy:Studies on residual stresses in welded joints of aluminum alloys (1st report)
スポンサーリンク
概要
- 論文の詳細を見る
The purpose of this study was to obtain the basic data on distributions of residual stresses in various types of aluminum welded joints. In this paper, the effects of dimensions and heat input during welding operations on residual stress distributions of 5083-0 butt joints are discussed.The residual stresses were calculated from the strains which still remained when the welded joint was cut into sections to release the stresses. The strains were measured by using resistance strain gages.In conclusion, the following results were obtained:(1) As general properties of residual stresses in welding, high tensile residual stresses having the magnitude nearly as large as the yield strength of the material appeared near the bead in the direction parallel to the weld line. However, the stresses normal to the weld line were smaller than those parallel to the line.(2) The maximum value of tensile residual stress was related to the length of the welded joint, but not so much dependent on its width.(3) Little effect of the heat input was given on residual stresses.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.