ON THE RADII OF 180° COLD BEND OF 17S-O ALLOY SHEETS
スポンサーリンク
概要
- 論文の詳細を見る
Because of our lacking in any pefinite. materials regarding the Bend Radii of 17S-O Alloy Sheets, we tried the bending test on the Sheets-0.4-1.0, 2.0, 4.4, and 6.0mm thick, respectively.The materials were annealed at 300°-450°C for an hour and furnace cooled and air cooled.We carefully compared the test results with JIS, (Proposed Spec.) coming to the conclusion that Furnace Cooliing after Annealing to 350°-400°C is necessary in order to get a good workability.