A STUDY OF PREVENTION FOR CONTACT CORROSION OF LIGHT METALS
スポンサーリンク
概要
- 論文の詳細を見る
Some test pieces were in such a way that on the both surfaces at the middle of 52S-0 sheets, bare and anodized, having 1mm thickness, 1mm. thick mild steel sheets are fixed on by means of bars rivets. The surface of the said mild steel sheets was treted in different ways, namely Zn dipping, Zn plating, Cd plating, Zinc-chromate coating and Bituminous painting. These test pieces were left wholly immersed in a bath of 5.85%NaCl+0.3%H2O2 solution for 3 months. Thenafter we have made their appearance as well as mechanical property tests.As the results, it was found that the test piece having the mild steel sheet with Bituminous paint proved the best.52S sheet with anodized surface gave a some what worse result than the bare one. Needless to say, the sample with bare 52S and bare mild steel sheets was showed to be the worst.By the way, it seems that in these contact corrosion test, NaCl testing solution with the addition of 0.3%H2O2 had rather too strong action.We have to add that these tests have been effected as a part of the collaborated tests of the Surface Treatment Sub-Committee of the Ship-Building Light Metal Committee.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.