Age hardening process of the AC4CH casting alloy solution treated at 843K was investigated mainly in view of aging temperatures. About 5 to 10% improvement of the tensile properties were obtained for the aging treatment at 418K for longer aging time as compared with those of the alloys heat treated with the conventional conditions. The percent elongation to the fracture and the absorbed energy, however, were not effectively improved. Reasonable correspondence between 0.2% proof stress and the specific resistance ratio were obtained. The proof stress was higher for the specimens aged at lower temperatures, although the resistance ratios were identical. The calculated m values of the Johnson-Mehl's equation for the precipitating particles were different for higher and lower temperatures, suggesting that the growth behavior of the particles was elassified into two types.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.