単ロ-ル急冷凝固法によるアルミニウム合金広幅クラッド箔の製造および箔特性
スポンサーリンク
概要
- 論文の詳細を見る
A single roll unit for rapid solidification of wide clad aluminum foils was designed and assembled. Two nozzles were attached tandem over the roll to produce clad foils. These nozzles have positional freedoms for the roll to investigate influences of the nozzle position on the clad foil formation. High purity aluminum and Al-4mass%Si, Al-12mass%Si and Zn-22mass%Al alloys were used. A molten alloy was poured by nitrogen pressure at 0.01 to 0.3MPa onto the roll rotating at 55m/s through the first nozzle, and another alloy was poured onto the first flow through the second nozzle. Clad aluminum alloy foils are succesfully prepared. A linear and undisturbed interface lies between the base foil and the overlying foil, acros which unappreciable alloying elements diffuse. The base and overlying foils are not teared each other by repeated bending.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.