Influence of electrolyte on the development of .GAMMA.'-alumina in the barrier oxide layers formed on aluminum covered with a thin layer of thermal oxide.
スポンサーリンク
概要
- 論文の詳細を見る
The development, during anodizing, of γ'-alumina within the barrier oxide layer formed on aluminum covered with a thin thermal oxide layer is strongly influenced by the nature of anion species of the electrolytes. The development of γ'-alumina is strongly inhibited when the thermally oxidized aluminum specimens were anodized in such solutions as aqueous ammonium dihydrogen phosphate, ammonium tartrate and ammonium citrate, where anion species of the respective electrolytes are known to exhibit inward movement after they have been incorporated into the growing barrier oxide layer. In such cases, the fine crystals of γ-alumina, which are thought to act as nuclei for the amorphous to crystalline transformation, are likely present surrounded by the amorphous film material doped with anion species of the electrolytes. The strong inhibition for the development of γ'-alumina can be explained as being due to the presence of the incorporated anions which are known to hinder the structural rearrangement at the amorphous/crystalline boundary.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.