Behavior of dislocations and hardening mechanisms in Al-Li alloys.
スポンサーリンク
概要
- 論文の詳細を見る
Deformation induced substructures of aged Al-Li alloys containing coherent δ'-L12 ordered particles were studied by dark field transmission electron microscopy. Dislocations move as pairs when fine scale precipitation of δ'-particles occurs. The form and distance of pair dislocations strongly depends on the size and distribution of particles. Particles having the diameters less than apporoximatery 50nm can be sheared by dislocation pairs. When the particles grow larger, dislocations by-pass the particles leaving the dislocation loops around them. Basing upon the observed behavior of dislocations, strengthening mechanisms in the Al-Li alloys were discussed taking into account the various resistances to the dislocation movement in the alloys. Main contributions to the strength of the alloy come from the energy of antiphase boundary and the frictional stress in the ordered particles. The measured yield strength and observed arrangements of deformation induced dislocations well agree with the theoretical proposal.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.