概要
- 論文の詳細を見る
Influences of sodium hydroxide and sodium aluminate concentrations, stirring velocity, temperature and particle size of the ores were studied. The leaching reactions gradually proceed with the prolonged leaching time. The leaching rates are accelerated by increasing the sodium hydroxide concentration and the surface area. The apparent activation energies calculated from the Arrhenius plots are 19.6, 17.1, 10.5 and 12.5kcal/mol for gibbsite, boehmite, Seaba ore and Comalco ore respectively. The leaching rates are independent of the stirring velocity and addition of sodium aluminate into the leaching solution. The rate-determing step in the leaching reactions of gibbsite, boehhite and buxite ores is a chemical reaction process rather than mass transport one. The leaching rates for gibbsite and boehmite are expressed as K.A.CNaOH. exp (-19600/1.987T) and K.A.CNaOH. exp (-17100/1.987T) respectively, where K is the rate constant, A the surface area of aluminumhydroxide, CNaOH the sodium hydroxide concentrationand T the absolute temperature.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.