5083アルミニウム合金の疲れ強さに及ぼす表面きずの影響
スポンサーリンク
概要
- 論文の詳細を見る
The fatigue strength of 5083-R and 5083-O sheet specimens of 6mm thickness having artificial scratches at the middle part was investigated. The scratch was made by scraping with a tool, having a tip angle of about 80° and a tip radius of about 0.02mm.As the results of tests, the effect of scratches on the fatigue strength was not found for the scratch depth less than 0.06mm for 5083-R specimens and less than 0.10mm for 5083-O, and fatigue fracture always occurred at the other part than the scratches. For the specimens with the scratch depth more than the above mentioned, fatigue failure was initiated at the surface scratches and their fatigue strength was slightly decreased with increasing the scratch depth. The effect of the angle between the scratch and the direction of the alternating stress on the fatigue strength was not found from the fatigue tests of 5083-O specimens with the scratch depth less than 0.2mm.
- 一般社団法人 軽金属学会の論文
一般社団法人 軽金属学会 | 論文
- Mechanical and wear properties of SiC whisker/ADC12 aluminum alloy composites fabricated by die casting.
- Joining of aluminum and ceramics.
- タイトル無し
- Undercooling and solidification behavior of fluid clumps of second-poured melt of hypereutectic Al-Si alloy in Duplex Casting process.
- Change in apparent viscosity of stirred slurry during production of semi-solid hypereutectic Al-Si alloy by slurry-melt mixing process.