Biodegradation Behavior of Poly (L-lactic acid) /Bran Blend in a Land-fill Test
スポンサーリンク
概要
- 論文の詳細を見る
Land-fill test of poly (L-lactic acid) blended with wheat bran (PLA/Bran blend) was carried out at two places, Kanazawa and Tsukuba (Japan). The test pieces were prepared by injection molding method. The mechanical properties in the blend sample considerably decreased with exposure time as compared with that of non-blended PLA. Further the molecular weight of PLA in the blended one decreased in one month. On the other hand, that of non-blended PLA hardly decreased under the same conditions. The number of microorganism on the surface of the blended test piece was from 100 to 10000 times as many as that on the non-blended one. The decrease of mechanical properties in the blend can be attributed to the effect of microorganism. Additionally, any clear difference was not observed in the results between Kanazawa and Tsukuba, though the humidity and the temperature of these places in the atmosphere were different from each other in winter.
- マテリアルライフ学会の論文
マテリアルライフ学会 | 論文
- オーステナイト系ステンレス鋼の局部腐食に及ぼす圧延加工の影響
- 新規複合サイクル試験による各種外装用塗装鋼板の耐久性評価
- 新規複合サイクル試験機による外装用塗装鋼板の耐久性評価方法の検討
- ポリウレタンの燃焼性と熱分解
- 酸化劣化ポリプロピレンを分散剤として利用したポリプロピレン/セルロース系ウッドプラスチックの改良