Effects of Density and Heat Treatment Temperature on Wear Performance of C/C Composites.
スポンサーリンク
概要
- 論文の詳細を見る
High-speed frictional tests of C/C composites having different densities and the final heat treatment temperatures have been studied. It was found that the wear resistance of C/C composites expressed by the number of tests increased with the increase of the densities at heat treatment temperatures (HTT) 1873 and 2273K, while this value decreased at HTT 2473K when the density was high. It was confirmed from the analysis of the experimental results that the best value for wear resistance of C/C composites was obtained at the average atomic face lattice distance d<SUB>(002)</SUB> was 0.339 to 0.340nm.