Bi<SUB>12</SUB>Si0<SUB>20</SUB> ITC Image Conversion Device
スポンサーリンク
概要
- 論文の詳細を見る
Bi<SUB>12</SUB>SiO<SUB>20</SUB> Incoherent-To-Coherent image conversion devices (abbreviated as BSO-ITC devices) are the most suitable devices for optical image processing systems, because of their high sensitivity and rather small half-wave voltage. In order to develop high storage capacity BSO-ITC devices, a 50mm-diameter BSO single crystal with good properties was grown with the newly developed crystal pull-ing system. This crystal was fabricated into an ITC device with 35×35mm<SUP>2</SUP> active area and 200, um to 400μm thickness. The write-in sensitivity to produce 1/100 output intensity decay was 2, 000 erg/cm<SUP>2</SUP>. Modulation Transfer Function which was measured by optical Fourier transform of a coherent read-out image was 0.5 at the spatial frequency of 15-20 1p/mm. The total storage capacity was 525 1p × 525 1p and comparable to that of a high resolution vidicon.
- 社団法人 レーザー学会の論文
社団法人 レーザー学会 | 論文
- Possible Isotope Separation by a Process of Nuclear Excitation by Electron Transition
- Integrated Optic Flow Meter with Cantilever Structure on Silicon Substrate.
- タイトル無し
- Application of Tunable Vacuum-Ultraviolet Laser to Chemical Reaction Dynamics.
- タイトル無し